Color Change and Physical-Mechanical Properties of Polystyrene-Impregnated Glulam from Three Tropical Fast-Growing Wood Species

Abstract

The aims of this work were to determine the color change and physical–mechanical properties of polystyrene glulam from three tropical wood species. Wood laminas were cut from logs harvested from a young plantation forest of manii (Maesopsis eminii), mangium (Acacia mangium), and rubber-wood (Hevea brasiliensis). The laminas were impregnated with monomer styrene that was polymerized using potassium peroxy-disulfate as a catalyst and heat. Three-layer glulam was constructed from the polystyrene laminas, using isocyanate glue and cold press. For comparison purposes, three-layer untreated glulam and solid wood samples were prepared. The results showed that the color change of polystyrene glulam was very small compared with untreated glulam. Polystyrene glulam had the highest density, while the density of untreated glulam did not differ from that of the solid wood. The moisture content of all products was matched to the environment, and fulfilled the Japanese standard. Compared with both types of glulams, solid wood had lower values for modulus of rupture (MOR), modulus of elasticity (MOE), and hardness, but higher shear strength. Meanwhile, polystyrene glulam had lower values for MOR and MOE, equal shear strength and wood failure, and higher hardness than the untreated glulam. All glulams had very little delamination in the hot water test. Only rubber-wood glulams fulfilled JAS 234-2003 for MOR, MOE, shear strength, and delamination. To obtain adequate physical–mechanical properties of glulams, medium-density wood is recommended for glulam manufacturing.