Consequences of Different Mechanical Surface Preparation of Ni-Base Alloys during High Temperature Oxidation

Abstract

The influence of surface roughness on its high temperature oxidation for an Ni-base superalloy was studied using laser profilometry, atomic force microscopy, mass change measurements, glow-discharge optical emission spectrometry, scanning electron microscopy, X-ray diffraction, and positron annihilation methods. The isothermal and cyclic air oxidation tests were performed at 1000 °C and showed dependence of oxidation behavior on surface roughness. Smoother surfaces oxidation resulted in the formation of a multilayered oxide scale consisting of NiO, Cr₂O₃, and internally oxidized Al₂O₃ while a rougher surface formed protective Al₂O₃ scale. The factors responsible for different oxidation behaviors were determined as higher concentration of vacancies and increased residual stresses in the near-surface region of studied alloys.