Materials & Design · 2020 · 218 citations · 52 references
EngineeringManufacturing EngineeringMaterials EngineeringManufacturing ProcessesMaterials CharacterizationSurface EngineeringLaser Material ProcessingLaser Surface ProcessingResidual StressSolidification CrackingSurface RoughnessWork HardeningFatigue FailureProcess Parameter EffectsProcess Parameter OptimizationProcess ParametersProcess Parameters OptimizationSelective Laser MeltingSurface Residual StressSurface Roughness Parameters
Selective laser melting of Inconel 718 has been studied mainly for density, while surface roughness and residual stresses remain underexplored, prompting the development of process maps to guide parameter selection for all three properties. The study aims to evaluate how varying laser power, scan speed, and hatch spacing affect density, surface roughness, and residual stresses in SLM of Inconel 718. The authors tested five laser powers, six scan speeds, and three hatch spacings selected from stable single‑track experiments to map their effects. The experiments showed that while individual parameters can yield up to 99.5% density, 2 µm roughness, or 248 MPa residual stress, no single setting optimizes all three, and a compromise of 99.2% density and 3.5 µm roughness at 320 W, 600 mm s⁻¹, 0.12 mm hatch spacing.
The current study investigates the effects of a wide range of process parameters on three part properties; density, surface roughness, and surface residual stresses simultaneously for selective laser melting of Inconel 718. In addition to the lack of investigations on surface roughness and residual stresses in selective laser melting of Inconel 718, process maps were developed for the selection of the best process parameters to achieve the desired values for the three parameters combined. Five laser powers, six scan speeds and three hatch spacings were chosen from the stable single tracks tests. Based on each property, a 99.5% density or a 2 μm surface roughness or the least surface tensile residual stress of 248 MPa were possible. However, no single process parameter combination was able to achieve good values for all three parameters. Prioritizing density and surface roughness, being crack initiators, over residual stresses for their effect on fatigue failure, it was found that 99.2% density and relatively low roughness of 3.5 μm are feasible at 320 W, 600 mm/s and 0.12 mm hatch spacing. Finally, opposite to the commonly observed columnar grain in Inconel 718, mixed grain structure was obtained at 600 mm/s and 1000 mm/s, indicating reduced anisotropy.
52