Transactions of the Iron and Steel Institute of Japan · 1978 · 153 citations · 0 references
EngineeringMaterials EngineeringMaterials ScienceHeat TransferThermal AnalysisThermodynamicsCastingCasting SolidificationFracture MechanicsHeat-affected ZoneMetal CastingSolidification CrackingAustenite TransformationCracksGrain BoundariesHysteresisThermal CrackingThermal Fracture MechanicsThermal Hysteresis
In order to redllce the occurrellce oj suiftlCe difects oj a cOlltillUOUS castillg slab, the most suitable secolldary coolillg pattern was de filled all the basis oj the results oj a theoretical calCillalioll allri a laboratory scale ex-Ilerimellt all the thermal hysteresis similar to those oj cOlltilluous castillg slabs. M oreover, i t has been considered ill this study that the trallsverse corner cracks could be relaled to the p resellce oj precipitates appeared ill the austenite grain boundaries.