In₂Se₃ Visible/Near-IR Photodetector With Observation of Band-Edge in Spectral Response

Abstract

We report on the demonstration of visible/near-IR high-performance photodetector based on exfoliated β-Indium selenide (In <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Se <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> ) on sapphire with a clear signature of band edge in spectral responsivity at a wavelength of ~850-900 nm. Room temperature photoluminescence (PL) measurements also indicated a peak at ~900 nm confirming the band-edge. Devices with inter-digitated metal-semiconductor-metal (MSM) geometry exhibited a responsivity of 3.8 A/W (normalized to device area). A low dark current of 0.80 nA and a photo to dark current ratio of ~52 were measured when illuminated with 650 nm A specific detectivity of 1 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">10</sup> cm Hz <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.5</sup> W <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> at 650 nm and 6 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">8</sup> cm Hz <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.5</sup> W <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> at the band-edge of 900 nm were estimated. These results indicate the promise of β-(In <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Se <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> ) for visible/near-IR detector applications.