Micro-Brazing of Stainless Steel Using Ni-P Alloy Plating

Abstract

A Ni-P plated layer of 20 μm thickness containing 11 wt.% P was formed on the surface of a stainless steel (SUS304) plate by electroplating. The microstructure and joint strength of the brazed joint with the electroplated Ni-11P layer were investigated. The results indicated that the filler metal was homogeneously distributed between the SUS304 plates and no voids or flaws formed in the brazed filler zone. Fe-Ni-Cr solid solutions were formed at the brazed interface. Moreover, P was mainly concentrated in such brazed filler zone to form P-containing phases. The average shear strength of the brazed joints was determined to be 47.3 MPa. The results demonstrated that the brazing of SUS304 plates using the electroplated Ni-11P layer as the filler metal was successfully realized.