Mechanical Properties of a Water Hyacinth Nanofiber Cellulose Reinforced Thermoplastic Starch Bionanocomposite: Effect of Ultrasonic Vibration during Processing

Abstract

Thermoplastic starch (TPS) reinforced by 1 wt % nanofiber cellulose (NFC) reinforcing from water hyacinth was produced. Ultrasonic vibration time (UVT) was applied to bionanocomposites during gelation for 0, 15, 30 and 60 min. Morphology of the NFC was investigated using Transmission Electron Microscopy (TEM). Scanning Electron Microscopy (SEM) and tensile tests were performed to identify the fracture surface and determine the mechanical properties of the bionanocomposites, respectively. The Crystallinity index (CI) of untreated and treated bionanocomposites was measured using X-ray Diffraction (XRD). The average diameter of NFC water hyacinth was 10–20 nm. The maximum tensile strength (TS) and modulus elasticity (ME) of the bionanocomposite was 11.4 MPa and 443 MPa respectively, after 60 min UVT. This result was supported by SEM which indicated good dispersion and compact structure.