Microstructural and XRD Analysis and Study of the Properties of the System Ti-TiAl-B4C Processed under Different Operational Conditions

Abstract

High specific modulus materials are considered excellent for the aerospace industry. The system Ti-TiAl-B4C is presented herein as an alternative material. Secondary phases formed in situ during fabrication vary depending on the processing conditions and composition of the starting materials. The final behaviors of these materials are therefore difficult to predict. This research focuses on the study of the system Ti-TiAl-B4C, whereby relations between microstructure and properties can be predicted in terms of the processing parameters of the titanium matrix composites (TMCs). The powder metallurgy technique employed to fabricate the TMCs was that of inductive hot pressing (iHP) since it offers versatility and flexibility. The short processing time employed (5 min) was set in order to test the temperature as a major factor of influence in the secondary reactions. The pressure was also varied. In order to perform this research, not only were X-Ray Diffraction (XRD) analyses performed, but also microstructural characterization through Scanning Electron Microscopy (SEM). Significant results showed that there was an inflection temperature from which the trend to form secondary compounds depended on the starting material used. Hence, the addition of TiAl as an elementary blend or as prealloyed powder played a significant role in the final behavior of the TMCs fabricated, where the prealloyed TiAl provides a better precursor of the formation of the reinforcement phases from 1100 °C regardless of the pressure.