Femtosecond and Attosecond Electron-Transfer Dynamics in PCPDTBT:PCBM Bulk Heterojunctions

Abstract

Charge separation efficiency is a crucial parameter for photovoltaic devices-polymers consisting of alternating electron-rich and electron-deficient parts can achieve high such efficiencies, for instance, together with a fullerene electron acceptor. This offers a viable path toward solar cells with organic bulk heterojunctions. Here, we measured the charge-transfer times in the femtosecond and attosecond regimes via the decay of sulfur is X-ray core excited states (with the core-hole clock method) in blends of a low-band gap polymer {PCPDTBT [poly[2,6-(4,4-bis (2-ethylhexyl)-4H-cyclopenta [2,1-b;3,4-1/1 dithiophene)-alt-4,7- (2,1,3-benzothiadiazole)]]} consisting of a cyclopentadithiophene electron-rich part and a benzothiadiazole electron-deficient part. The constituting parts of the bulk heterojunction were varied by adding the fullerene derivative PCBM ([6,6]-phenyl-C-61-butyric acid methyl ester) (weight ratio of polymer/PCBM as 1:0, 1:1, 1:2, and 1:3). For low-energy excitations, the charge-transfer time varies to the largest extent for the thiophene donor part. The charge-transfer time in the 1:2 blend is reduced by 86% compared to that of pristine PCPDTBT. At higher energy excitations, the charge-transfer time does not vary with the chemical environment, as this regime is dominated by intramolecular conduction that yields ultrafast charge-transfer times for all blends, approaching 170 as. We thus demonstrate that the core-hole clock method applied to a series with changing composition can give information about local electron dynamics (with chemical specificity) at interfaces between the constituting parts the crucial part of a bulk heterojunction where the initial charge separation occurs.