Unique crystallization behavior of sodium manganese pyrophosphate Na₂MnP₂O₇ glass and its electrochemical properties

Abstract

sCrystallization behavior of Na2MnP2O7 precursor glass was examined. Layered type Na2MnP2O7 was formed at 461 °C for 3 h in N2 filled electric furnace. Irreversible phase change was confirmed from layered Na2MnP2O7 to β-Na2MnP2O7 over 600 °C. At 650 °C crystallized phase was completely changed to β-phase. By means of charge and discharge testing it is found that layered Na2MnP2O7 is also active as cathode in sodium ion batteries. We found glass-ceramics technology is one of the suitable process for the synthesis of layered Na2MnP2O7 cathode without any complicate process.