Preparation of NiCoP Hollow Quasi-Polyhedra and Their Electrocatalytic Properties for Hydrogen Evolution in Alkaline Solution

Abstract

Double metal phosphide (NiCoP) with hollow quasi-polyhedron structure was prepared by acidic etching and precipitation of ZIF-67 polyhedra and further phosphorization treatment with NaH 2 PO 2 . The morphology and microstructure of NiCoP quasi-polyhedron and its precursors were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and a micropore and chemisorption analyzer. Electrocatalytic properties were examined by typical electrochemical methods, such as linear sweep voltammetry, cyclic voltammetry, chronoamperometry, and electrochemical impedance spectroscopy in 1.0 M KOH aqueous solution. Results reveal that, compared with CoP hollow polyhedra, NiCoP hollow quasi-polyhedra exhibit better electrochemical properties for hydrogen evolution with a low onset overpotential of 74 mV and a small Tafel slope of 42 mV dec –1 . When the current density is 10 mA cm –2, the corresponding overpotential is merely 124 mV, and 93% of its electrocatalytic activity can be maintained for 12 h. This indicates that NiCoP with hollow quasi-polyhedron structure, bimetallic merit, and low cost may be a good candidate as electrocatalyst in the practical application of hydrogen evolution.