Crystal-Orientation-Modulated Exchange Bias in Orthorhombic-YMnO₃/La_0.6Sr_0.4MnO₃ Multiferroic Heterostructures

Abstract

The magnetic properties of the all-oxide multiferroic heterostructures composed of orthorhombic YMnO3 (YMO) with E-type antiferromagnetic and double-exchange ferromagnetic (FM) La0.6Sr0.4MnO3 (LSMO) were studied. An orientation-modulated exchange bias effect, which is related to the interfacial Mn-O-Mn bond angle, was discovered. Because of the large bond angle in YMO/LSMO(100) heterostructures, a strong exchange coupling at the interface is formed. This strong exchange coupling sustains an FM phase in YMO at the interface region. The FM phase with strong magnetocrystalline anisotropy contributes to the vertical shift and exchange bias effect in (100) orientation heterostructures. When LSMO (110) and (111) were layered with YMO, the Mn-O-Mn bond angle was reduced, leading to a weakened exchange coupling at the interface, and only a relatively small exchange bias at low temperatures was visible.