Cellulose‐Based Ionogels for Paper Electronics

Abstract

A new class of biofriendly ionogels produced by gelation of microcellulose thin films with tailored 1‐ethyl‐3‐methylimidazolium methylphosphonate ionic liquids are demonstrated. The cellulose ionogels show promising properties for application in flexible electronics, such as transparency, flexibility, transferability, and high specific capacitances of 5 to 15 μF cm −2 . They can be laminated onto any substrate such as multilayer‐coated paper and act as high capacitance dielectrics for inorganic (spray‐coated ZnO and colloidal ZnO nanorods) and organic (poly[3‐hexylthiophene], P3HT) electrolyte‐gated field‐effect transistors (FETs), that operate at very low voltages (<2 V). Field‐effect mobilities in ionogel‐gated spray‐coated ZnO FETs reach 75 cm 2 V −1 s −1 and a typical increase of mobility with decreasing specific capacitance of the ionogel is observed. Solution‐processed, colloidal ZnO nanorods and laminated cellulose ionogels enable the fabrication of the first electrolyte‐gated, flexible circuits on paper, which operate at bending radii down to 1.1 mm.