Transformation of brookite-type TiO2 nanocrystals to rutile: correlation between microstructure and photoactivity

Abstract

Nanometric particles of pure brookite TiO2 were synthesized by modified thermolysis of reactant solutions containing titania powder, HCl, urea and PEG 10000. Unique flower-like brookite agglomerates with an average diameter of ∼400–450 nm composed of single brookite nanocrystals of ∼4–5 nm were obtained at 105 °C. The brookite → rutile transformation has been studied and TiO2 mixtures with variable amount of anatase, brookite and rutile polymorphs at different temperatures (from 200 to 800 °C) were obtained. High resolution transmission electron microscopy (HRTEM), electron diffraction pattern and BET/BJH analyses were used to characterize the phase assemblages, crystallite size and pore volume of the pure-phase brookite and TiO2 mixtures. In order to understand the metastable–stable TiO2 phase transformation X-ray powder diffraction (XRD) was performed. The photoactivity of pure brookite and TiO2 powders with different compositions of the brookite–anatase–rutile and anatase–rutile polymorphs obtained during the transitions was examined by photocatalyzed degradation of 4-chlorophenols in aqueous solution. The titania sample having the highest catalytic activity was obtained at 500 °C, contained 3.2% brookite, 42.9% anatase and 53.9% rutile and is referred to as TiO[B])/500 .