Bone response to radio frequency sputtered calcium phosphate implants and titanium implants <i>in vivo</i>

Abstract

The objective of this study was to evaluate the effect of radio frequency sputtered calcium phosphate (CaP) coatings of titanium (Ti) implants on the bond strength at the bone-implant interface and percent bone contact length. Cylindrical coated or noncoated implants (4.0-mm diameter by 8-mm long) were implanted for 3 and 12 weeks. At 3 weeks after implant placement, the ultimate interfacial strengths for as-deposited CaP-coated and heat-treated CaP-coated implants were 2.29 +/- 0.14 MPa and 1.28 +/- 0.04 MPa, respectively. These ultimate interfacial strength values at 3 weeks were statistically greater than the mean ultimate interfacial strength for control Ti implants (0.67 +/- 0.13 MPa). At 12 weeks after implant placement, no statistical differences in the mean ultimate interfacial strengths were observed between the as-deposited CaP-coated, heat-treated CaP-coated, and control Ti implants. Histomorphometric evaluation indicated greater percent bone contact lengths for the as-deposited CaP-coated implants compared with the heat-treated CaP-coated and control Ti implants 3 and 12 weeks after implant placement.