Nanosize Powders of Aluminum Nitride Synthesized by Pulsed Wire Discharge

Abstract

Nanosize particles of aluminum nitride have been successfully synthesized by a pulsed wire discharge (PWD). Intense pulsed current through an aluminum wire evaporated the wire to produce a high‐density plasma. The plasma was then cooled by an ambient gas mixture of NH 3 /N 2 , resulting in nitridation. As a result, nanosize particles of aluminum nitride were formed. The average particle diameter was found to be ∼28 nm with a geometric standard deviation of 1.29. The maximum AlN content of 97% in the powders was achieved by optimizing various parameters: the gas pressure, the ratio of NH 3 and N 2 , the wire diameter, the pulse width, and the input electrical energy. The ratio of the AlN powder production to the electrical energy consumption was evaluated as ∼40 g/(kW·h). Thus, PWD is a very efficient and promising method to synthesize nanosize powders of AlN.