Reduction of Efficiency Droop in InGaN Light-Emitting Diode Grown on Self-Separated Freestanding GaN Substrates

Abstract

Using a GaN nanorod template in a hydride vapor phase epitaxy (HVPE) system can manufacture a freestanding GaN (FS-GaN) substrate with threading dislocation densities down to ~ 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">7</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> . In this letter, we report InGaN/GaN multiple-quantum-well light-emitting diodes (LEDs) grown on this FS-GaN substrate. The defect densities in the homoepitaxially grown LEDs were substantially reduced, leading to improved light emission efficiency. Compared with the LED grown on sapphire, we obtained a lower forward voltage, smaller diode ideality factor, and higher light-output power in the same structure grown on FS-GaN. The external quantum efficiency (EQE) of LEDs grown on FS-GaN were improved especially at high injection current, which brought the efficiency droop phenomenon greatly reduced at high current density.