Electrochemical Properties of Yolk–Shell‐Structured CuO–Fe₂O₃ Powders with Various Cu/Fe Molar Ratios Prepared by One‐Pot Spray Pyrolysis

Abstract

Several yolk-shell-structured CuO-Fe2 O3 powders with various Cu/Fe molar ratios have been successfully prepared under equivalent reaction conditions using a one-pot spray pyrolysis process. The Cu and Fe components are uniformly distributed throughout the powders, irrespective of composition. The Brunauer-Emmett-Teller surface areas of the yolk-shell CuO-Fe2 O3 systems increased from 5 to 16 m(2) g(-1) if the Cu/Fe molar ratios are decreased from 3:1 to 1:3. The initial discharge and charge capacities of the yolk-shell CuO-Fe2 O3 system (Cu/Fe=1:2), showing maximum values at a constant current density of 1000 mA g(-1) , are 1436 and 1012 mA h g(-1) , respectively. After 130 cycles, the discharge capacities of the yolk-shell CuO-Fe2 O3 powders with Cu/Fe molar ratios of 1:3, 1:2, 1:1, 2:1, and 3:1 are 1159, 1151, 755, 655, and 651 mA h g(-1) , respectively. The discharge capacities of the yolk-shell and dense powder samples after 50 cycles, when subjected to a series of current density increases from 500 to 5000 mA g(-1) , are 735 and 495 mA h g(-1) , respectively.