Rapid carbothermal reduction of boron oxide in a graphite transport reactor

Abstract

Abstract Uniform submicron crystals of B 4 C, boron‐enriched boron carbide, and B 4 C/TiB 2 composite powders have been synthesized continuously by rapid carbothermal reduction at approximately 2,200 K in a 0.14 m ID × 1.68 m long pilot‐scale graphite transport reactor. A unique reactor design allowed for continuous feeding of a meltable boron oxide containing precursor, rapid heating rates that completed the carbothermal reduction reaction in seconds, and an expanded cooling that allowed for the precipitation in space of volatile excess boron oxides. Powder morphology resembled that of powder synthesized by laser pyrolysis of gaseous reactants. Rapid heating rates and minimized reaction times at high temperatures promoted nucleation with limited crystal growth. Dense parts fabricated from these powders had fine grains and extreme hardness.