Reactive extrusion of polycaprolactone compounds containing wood flour and lignin

Abstract

Abstract Biodegradable polycaprolactone (PCL) was melt‐compounded in a Werner & Pfleiderer twin‐screw extruder (ZSK25) together with wood flour (WF) and lignin with maleic anhydride‐grafted polycaprolactone (PCL‐ g ‐MA) used as a compatibilizer. The grafting of maleic anhydride onto PCL was achieved with reactive extrusion in the presence of 2,5‐dimethyl‐2,5‐di‐( t ‐butylperoxy)hexane as an initiator. The graft copolymers were analyzed with size exclusion chromatography and titration. As a function of the initiator and maleic anhydride addition, the grafted maleic anhydride content varied from 1.4 to 3.1 wt %. Compounds compatibilized with PCL‐ g ‐MA exhibited improved mechanical properties: a compatibilized PCL compound containing 40 wt % WF gave a Young's modulus of 2300 MPa with respect to 400 MPa for neat PCL and a 100% increase in yield stress. The content of WF, lignin, and PCL‐ g ‐MA was varied systematically to examine stress–strain and impact behavior. Low contents of grafted maleic anhydride and PCL‐ g ‐MA were required to improve both mechanical properties and interfacial adhesion. Biodegradation was investigated. Lignin addition was found to retard biodegradation. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 81: 1972–1984, 2001