Preparation of a bio-based epoxy with comparable properties to those of petroleum-based counterparts

Abstract

In this paper a bio-based epoxy with outstanding thermal and mechanical properties was synthesized using a rosin-based epoxy monomer and a rosin-based curing agent. The chemical structures of rosin based epoxy monomer and curing agent were confirmed by Nuclear Magnetic Resonance (NMR) and Fourier Transform Infrared (FT-IR) spectra. The flexural mechanical and dynamic mechanical properties as well as thermal stability of the cured epoxy were investigated. The results showed that the cured epoxy exhibited a glass transition temperature (T g ) of 164C and its flexural strength and modulus were as high as 70 and 2200 MPa, respectively. This indicated that a wholly bio-based epoxy resin possessing high performance was successfully obtained.