Some electrical and optical studies in CsCuCl3 crystals

Abstract

The optical absorption spectra and some electrical properties of CsCuCl3single crystals have been studied in a wide temperature range. In the visible region the absorption is characterized by a dichroic charge transfer band. In the near infrared region three absorption bands are found at 8300, 10000, and 12900 cm−1 and are attributed to transitions between the levels of a Cu2+ ion in a tetragonally distorted cubic field. Both the dielectric constant and dielectric loss measurements indicate appreciable anomalies at the transition point, 423 K. Conductivity measurements indicate a clear first order transition with different activation energies in the low and high temperature phases. Die optischen Absorptionsspektra und elektrischen Eigenschaften von CsCuCl3-Einkristallen wurden in einem weiten Temperaturbereich untersucht. Im sichtbaren Bereich des Spektrums wird die Absorption durch eine dichroitische Charge-Transfer-Bande bestimmt. Im nahen Infrarotbereich wurden drei Absorptionsbanden bei 8300, 10000 und 12900 cm−1 entdeckt und diese Banden als Übergänge zwischen den Energieniveaus des Cu2+-Ions im tetragonal gestörten, kubischen Feld erklärt. Sowohl die Messungen der dielektrischen Konstante als diejenigen der dielektrischen Verluste zeigen bedeutende Anomalien im Übergangspunkt, 423 K. Die Leitfähigkeitsmessungen zeigen einen klaren Übergang erster Ordnung, wobei sich die Aktivationsenergien der Phasen bei niedrigen und hohen Temperaturen erheblich voneinander unterscheiden.