Glancing angle deposition of Ge nanorod arrays on Si patterned substrates

Abstract

A periodic arrangement of Ge nanorods on a Si(111) substrate was realized by glancing angle deposition (GLAD) onto honeycomb-like arranged Au hillocks formed using a self-assembled monolayer of polystyrene nanospheres as an evaporation mask. Additionally, a honeycomb-like arrangement of Au dots was used as an etch mask in a reactive ion beam etching process for pattern transfer procedure. Resulting honeycomb patterns consisting of Si hillocks within the Si(111) substrates were utilized to deposit Ge nanorods. Effective morphological variations in shape and dimension of GLAD-grown nanorods on honeycomb-like patterned substrates with both Au dot and Si dot arrays are strongly influenced by interseed distances, seed heights, and consequently shadowing lengths. For a large pattern period, it was observed that the usual triangular shape of the nanorod changed to a hexagonal shape as an effect of additional particle flux that reached the growing nanorod from the direction of second and third-nearest neighbors due to inadequate shadowing lengths and increased interseed condensation.