Correlation between absorption bands and implanted alkali ions in LiF

Abstract

Defects induced in LiF by bombardment with alkali ions in the 1 MeV energy range have been investigated by optical absorption measurements. Inaddition to the absorption bands of F and F-aggregate centres, newbands have been obtained after thermal annealings and have been attributed to implanted ion centres. The corresponding absorption band positions depend on the nature of the implanted ions and have been obtained at 520 nm for sodium (CA(Na+) band) and 680 nm for potassium (CA(K+) band). The comparison of these band positions with those of the colloidal centres created in NaCl and KCl by ionbombardment suggests that they are colloidal bands. So it has been deduced from Doyle's theory that the CA bands were due to the plasma resonance of quasimetallic particles formed after precipitation of the implanted ions. Les défauts créés dans LiF par bombardement avec des ions alcalins d'énergie de l'ordre du MeV ont été étudiés par des mesures d'absorption optique. En plus des bandes d'absorption des centres F et agglomérats de F, de nouvelles bandes ont été obtenues après traitement thermique et ont été attribuées à des centres dus aux ions implantés. Les positions des bandes d'absorption correspondantes dépendent de la nature de l'ion implanté et ont été obtenues à 520 nm pour le sodium (bande CA(Na+)) et à 680 nm pour le potassium (bande CA(K+)). La comparaison entre les positions de ces bandes et celles des bandes colloïdales créés dans NaCl et KCl par bombardement ionique, nous a suggéré qu'elles étaient dues à la présence de colloïdes. La théorie de Doyle nous a permis de montrerque les bandes CA étaient dues à la résonance de plasma de particules quasimétalliques formées par la coagulation des ions implantés.