Strain-induced effects in colloidal quantum dots: lifetime measurements and blinking statistics

Abstract

A series of samples of CdSe/Cd(x)Zn(1-x)S core/shell quantum dots have been synthesized in order to measure the influence of lattice-mismatch-induced strain on the photoluminescence (PL) and blinking behaviour. The PL spectra show a significant variation of the fluorescence wavelength even though the colloidal quantum dots (cQDs) are similar in size. The PL excitation spectra show a gradual splitting of the first exciton level as the proportion of Zn is increased in the shell and as the shell grows. On the other hand, blinking studies clearly demonstrate a significant dependence on the amount of Zn present in the shell. Distributions of on and off times go from the usual power-law distributions to power-law distributions with exponential cut-offs. These cut-offs become increasingly pronounced as the proportion of Zn increases. We interpret these results in the framework of diffusion-controlled electron transfer. Exciton relaxation lifetime measurements strongly suggest that lattice mismatch is responsible for a greater number of defects in core/shell cQDs. Therefore, strain and lattice mismatch are shown to be parameters of significant importance for the electronic structure of nanocrystals, influencing the photoluminescence, exciton relaxation lifetime and blinking behaviour.