Applied Physics Letters · 2008 · 38 citations · 22 references
Natural SciencesMaterials EngineeringMaterials ScienceNanomaterialsNanotechnologySensorsChemical SensorsChemical Vapor DepositionNanosensorsNanostructured SurfacesSensor MaterialsSurface PhysicsMetalorganic Chemical Vapor DepositionNano SensorsNanomaterial-based SensorsNanostructured Sensor MaterialsNanostructured SensorsSelective SensingSensing ApplicationsTemperature-dependent Electrical Measurements
The hydrogen sensing characteristics of multiple InN nanobelts grown by metalorganic chemical vapor deposition were investigated. Pt-coated InN sensors could selectively detect hydrogen at the tens of ppm level at 25 °C, while uncoated InN showed no detectable change in current when exposed to hydrogen under the same conditions. Upon exposure to various concentrations of hydrogen (20–300 ppm) in N2 ambient, the relative resistance change increased from 1.2% at 20 ppm H2 to 4% at 300 ppm H2. Approximately 90% of the initial InN resistance was recovered within 2 min by exposing the nanobelts to air. Temperature-dependent measurements showed larger resistance change and faster response at high temperature compared to those at room temperature due to increase in catalytic dissociation rate of H2 as well as diffusion rate of atomic hydrogen into the Pt/InN interface. The Pt-coated InN nanobelt sensors were operated at low power levels (∼0.5 mW).
22
Hydrogen-selective sensing at room temperature with ZnO nanorods
H. T. Wang, B. S. Kang, F. Ren et al. · Applied Physics Letters · 2005 · 542 citations