Magnetic characterization and recording properties of patterned Co/sub 70/Cr/sub 18/Pt/sub 12/ perpendicular media

Abstract

A lithographically patterned magnetic medium is one of the proposed routes to magnetic recording at a density beyond that thought to be possible using conventional recording media due to thermal instability caused by superparamagnetism. Using a focused ion beam to pattern a granular Co/sub 70/Cr/sub 18/Pt/sub 12/ film, we have fabricated sub-80-nm size islands that are single domain and with a narrowed switching field distribution and an enhanced thermal stability. Magnetic isolation of the islands is shown to be a result of vanishing of magnetic remanence and coercivity in the irradiated region and not a result of sputtering. Recording measurements using a quasi-static giant magnetoresistive head demonstrate the sensitivity to detect single 80-nm islands. The readback jitter from the patterned region is dramatically reduced compared to that measured for continuous media at the same linear density.