Mechanical Behavior of Novel Suction Cast Ti-Cu-Fe-Co-Ni High Entropy Alloys

Abstract

The present investigation reports mechanical properties of novel multicomponent Ti x Cu y Fe 20 Co 20 Ni 20 high entropy alloys (HEAs) with different alloy chemistry (x/y = 1/3, 3/7, 3/5, 9/11, 1, 11/9 and 3/2). The alloy cylinders were prepared by vacuum arc melting-cum-suction casting route. The detailed electron microscopic observations reveal the presence of three different solid solution phases; FCC (a 1 ) phase, FCC (a 2 ) phase and BCC (b) phase for all the investigated alloys, whereas ultrafine eutectic between FCC (a 1 ) phase, and Ti 2 (Co, Ni) - type Laves phase has been observed for the HEAs with x/y = 9/11, 1, 11/9 and 3/2. Room temperature compression test of the suction cast cylinders with aspect ratio of 2/1 has been conducted to obtain mechanical properties of the HEAs. The optimum combination of strength (~ 1.88 GPa) and plasticity (~ 21 %) is obtained for x/y = 9/11; indicating simultaneous improvement of strength as well as plasticity of the novel HEAs. Fractographic analysis of the fractured surfaces reveals mixed mode of fracture for x/y = 1/3, 3/7 and 3/5, ductile mode for x/y = 9/11 and 1, whereas brittle mode of fracture for x/y = 11/9 and 3/2.