Solid solution alloys of AlCoCrFeNiTix with excellent room-temperature mechanical properties

Abstract

Alloys with composition of AlCoCrFeNiTix (x: molar ratio; x=0,0.5,1,1.5) were designed by using the strategy of equiatomic ratio and high entropy of mixing. The alloy system is composed mainly of body centered cubic solid solution and possesses excellent room-temperature compressive mechanical properties. Particularly for AlCoCrFeNiTi0.5 alloy, the yield stress, fracture strength, and plastic strain are as high as 2.26GPa, 3.14GPa, and 23.3%, respectively, which are superior to most of the high-strength alloys such as bulk metallic glasses.