High Current Density and Long-Life Nanocomposite Scandate Dispenser Cathode Fabrication

Abstract

A nano-Sc <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -added W powder for use in high current density thermionic cathodes has been made using a solution-gel method with the following controllable uniform average particle sizes: ~72, 146, 272, and 587 nm. Using these powders, nanostructured Sc <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -added tungsten matrices with uniform nanosized tungsten grains and homogenous pore distribution were obtained. Nanocomposite Sc <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -added W impregnated cathodes have been prepared from these powders and have shown excellent emission properties. For example, space-charge-limited current densities of 40 ± 1 A · cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> at 850°C and 170 ± 5 A · cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> at 1050°C have been obtained using a 300-nm Sc <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -added (4.77 wt.%) W powder. Life testing is ongoing with 50 ± 2.5 A · cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-2</sup> current density emission demonstrated at 1050°C after 10 680 h.