Room temperature flexible and transparent ITO/Ag/ITO electrode grown on flexile PES substrate by continuous roll-to-roll sputtering for flexible organic photovoltaics

Abstract

We prepared a flexible and transparent indium tin oxide (ITO)/Ag/ITO electrode on a polyethersulfone (PES) substrate using a specially designed roll-to-roll sputtering system at room temperature for use in flexible organic solar cells (OSCs). By the continuous roll-to-roll sputtering of the ITO and Ag targets, we fabricated a flexible ITO/Ag/ITO electrode with a sheet resistance (Rsh) of 4.28 Ω/square, optical transmittance (T) of 89.28% and figure of merit value of 75.03 × 10−3 Ω−1 at the optimized Ag thickness of 12 nm (dc power of 200 W) without breaking the vacuum, even though it was deposited at room temperature. The bending test results demonstrated that the ITO/Ag/ITO electrode has superior flexibility to the single ITO electrode, due to the high failure strain of the ductile Ag layer. Moreover, the flexible OSC fabricated on the optimized flexible ITO/Ag/ITO electrode showed an identical efficiency of 3.73% to the OSC fabricated on the commercial crystalline ITO electrode, due to its low sheet resistance and high transparency, which are well matched with the organic active layer. This indicates that the flexible ITO/Ag/ITO multilayer electrode grown by the continuous roll-to-roll sputtering technique is a promising flexible and transparent electrode for use in cost-efficient flexible OSCs.