BaTiO_3 thin-film waveguide modulator with a low voltage–length product at near-infrared wavelengths of 098 and 155 µm

Abstract

A BaTiO3 thin-film electro-optic waveguide modulator with a low half-wave voltage-length product has been demonstrated at near-infrared wavelengths of 1-1.6 microm. Half-wave voltage-length products as small as 0.25 and 0.5 V cm were measured for a 5-mm-long device at wavelengths of 973 and 1561 nm, respectively. The effective electro-optic coefficients were calculated as 420 pm/V at 973 nm and 360 pm/V at 1561 nm. Further improvements in device performance by optimizing the ferroelectric domain structure are anticipated.