Self-Assembly of Conjugated Polymers at the Air/Water Interface. Structure and Properties of Langmuir and Langmuir−Blodgett Films of Amphiphilic Regioregular Polythiophenes

Abstract

This paper provides the first direct structural evidence describing conjugated polymer self-assembly at the air−water interface. Grazing-incidence X-ray diffraction (GIXD) and X-ray reflectivity measurements on a number of derivatives of amphiphilic regioregular polythiophenes (e.g., poly(3‘-dodecyl-3-(2,5,8-trioxanonyl)-2‘,5-bithiophene), polymer 1 ) show that these conjugated polymers self-assemble as 2-dimensional polycrystalline monolayers at the air/water interface with the amphiphilic polymers preorganized into rigid boards standing edge-on on the water surface. The monolayer consists of highly ordered (∼70% crystalline) domains, with a centered rectangular unit cell having the polymer backbone along the a -axis and the thiophene π-stack along the b axis with a distance of 3.85−3.94 Å depending on the applied surface pressure. These domains are connected by soft, more disordered boundaries. This is evidenced by the macroscopic compressibility of the entire LB film ( C macro ≈ 4−7 m/N) being one order of magnitude larger than the microscopic compressibility ( C micro ≈ 0.6 m/N) of the polycrystalline domains. The alkyl chains in the 3-position of the thiophene rings are in a crystallographically disordered state due to their cross-sectional mismatch with the packing of the thiophenes. The importance of having the side chains coupled in a regioregular fashion to the 3-position of the thiophene rings is evidenced by a dramatic increase in the coherence length of the crystalline domains for highly regioregular samples (>95% head−tail couplings) as compared to less regioregularly coupled polymers (∼80% head−tail couplings). Transfer to solid support by the Langmuir−Blodgett technique induces an overall orientation of the domains in the film, giving rise to a dichroic ratio of up to 4. Reflection−absorption infrared spectroscopy (RAIRS) shows that the alkyl chains of transferred films are in an all- trans conformation with a locally ordered environment, having only few gauche defects.