Synthesis of Mesoporous Silica@Co–Al Layered Double Hydroxide Spheres: Layer-by-Layer Method and Their Effects on the Flame Retardancy of Epoxy Resins

Abstract

Hierarchical mesoporous silica@Co-Al layered double hydroxide (m-SiO2@Co-Al LDH) spheres were prepared through a layer-by-layer assembly process, in order to integrate their excellent physical and chemical functionalities. TEM results depicted that, due to the electrostatic potential difference between m-SiO2 and Co-Al LDH, the synthetic m-SiO2@Co-Al LDH hybrids exhibited that m-SiO2 spheres were packaged by the Co-Al LDH nanosheets. Subsequently, the m-SiO2@Co-Al LDH spheres were incorporated into epoxy resin (EP) to prepare specimens for investigation of their flame-retardant performance. Cone results indicated that m-SiO2@Co-Al LDH incorporated obviously improved fire retardant of EP. A plausible mechanism of fire retardant was hypothesized based on the analyses of thermal conductivity, char residues, and pyrolysis fragments. Labyrinth effect of m-SiO2 and formation of graphitized carbon char catalyzed by Co-Al LDH play pivotal roles in the flame retardance enhancement.