Ferromagnetic Resonance in Magnetite Thin Films

Abstract

We have been investigating the spin motive force induced by magnetization dynamics in ferromagnetic materials. Ferrimagnetic materials are expected to exhibit even larger spin motive force due to their spatially staggered magnetic structure and high frequency spin wave modes. We believe that magnetite (Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> ) is one of the candidates for this purpose. Here, we report magnetic resonance in Fe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> thin films epitaxially grown on a MgO (001) substrate. The gyromagnetic ratio and the effective saturation magnetization are estimated to be 1.71 ×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">11</sup> s <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> T <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> and 364 emu/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sup> , respectively. The Gilbert damping constant of 0.02 is obtained from the magnetic field dependence of the linewidth. We expect to investigate the spin motive force induced from this magnetic resonance.