Calorimetric studies on an anhydride‐cured epoxy resin from diglycidyl ether of bisphenol‐A and diglycidyl ether of poly(propylene glycol). I. Onset of diffusion control during isothermal polymerization

Abstract

Abstract Calorimetric studies on a series of anhydride‐cured epoxy resins, in which the epoxy oligomer is a mixture of diglycidyl ether of bisphenol‐A (DGEBA) and diglycidyl ether of poly(propylene glycol) (DGEPPG) in different mole ratios, were carried out. DGEPPG is a flexible epoxy oligomer that was used to tune glass transition temperature for the fully reacted epoxy resin. Conversion versus time curves for the systems with different DGEBA/DGEPPG mole ratios (not including the neat DGEPPG system) were found to overlap with each other in mass‐controlled reaction regime, indicating similar reactivities of epoxy groups in both epoxy oligomers. Onset of diffusion‐controlled reaction regime for different systems was estimated by fitting the conversion versus time data using a phenomenological kinetic equation, as well as from direct comparison of the conversion versus time curves. For the systems (i.e., 0, 10, and 30% DGEPPG) that vitrify during reaction, the crossover from mass‐controlled to diffusion‐controlled reaction occurs close to the onset of the vitrification, where T g is about 25–30 K below the reaction temperature. For the system (i.e., 50% DGEPPG system) that does not vitrify during the reaction, such crossover still occurs when the T g of the mixture reaches a value about 25 K below the reaction temperature. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2155–2165, 2008