A study on the radiation damage and recovery of neutron irradiated vessel steel using magnetic Barkhausen noise

Abstract

The radiation damage and thermal recovery characteristic of neutron irradiated SA508-3 reactor pressure vessel steel specimens have been investigated. Two recovery stages were identified from the results of hardness measurements during isochronal annealing and the mechanism responsible for the two stages was explained by using the results of Barkhausen noise measurement on the basis of the interaction between radiation induced defects and the magnetic domain wall. The coercivity was not changed by neutron irradiation, whereas the maximum magnetic induction increased. Barkhausen noise parameters associated with the domain wall motion were decreased by neutron irradiation and recovered with subsequent heat treatments.