Hydrogen sensing properties of protective-layer-coated single-walled carbon nanotubes with palladium nanoparticle decoration

Abstract

Protective-layer-coated single-walled carbon nanotubes (SWNTs) with palladium nanoparticle decoration (Pd-SiO(2)-SWNTs) were fabricated and their sensing properties for hydrogen (H(2)) were investigated. SWNTs were coated with a 3-4 nm thick SiO(2) layer by pulsed laser deposition and subsequently decorated with Pd nanoparticles by electron beam evaporation. Even though the SWNTs were completely surrounded by a protective layer, Pd-SiO(2)-SWNTs responded to H(2) down to a concentration of 1 part per million. Compared with the Pd nanoparticle-decorated SWNTs without a protective layer (Pd-SWNTs), Pd-SiO(2)-SWNTs exhibited highly stable sensor responses with variations of less than 20%; Pd-SWNTs showed a variation of 80%. The density of the Pd-SWNTs significantly decreased after the sensing test, while that of the Pd-SiO(2)-SWNTs with the netlike structure remained unchanged. The hydrogen sensing mechanism of the Pd-SiO(2)-SWNTs was attributed to the chemical gating effect on the SWNTs due to dipole layer formation by hydrogen atoms trapped at the Pd-SiO(2) interface. Moreover, the relationship between H(2) concentration and sensor response can be described by the Langmuir isotherm for dissociative adsorption.