Novel Zn_1-<i>_x</i>Mn<i>_x</i>Se (<i>x</i> = 0.1−0.4) One-Dimensional Nanostructures:  Nanowires, Zigzagged Nanobelts, and Toothed Nanosaws

Abstract

Novel Zn1-xMnxSe one-dimensional nanostructures-straight nanowires (x = 0.1 and 0.3), zigzagged nanobelts (x = 0.4), and toothed nanosaws (x = 0.4)-were synthesized using the chemical vapor deposition method. They all consisted of single-crystalline wurtzite ZnSe crystals, irrespective of the Mn content. In particular, the nanosaws have a unique structure in which double-sided teeth are rooted in the nanowire core and bent so as to align as two parallel rows. The long axis is parallel to the [010] direction, and all of the teeth have the [0001] growth direction. The X-ray diffraction pattern confirms the formation of wurtzite ZnSe crystal and the decrease of the lattice constant owing to Mn doping. The Mn2+ emission at 2.1 eV (appeared below 100 K), originating from the d-d (4T1 --> 6A1) transition, proves the effective substitution of Mn2+ ions at the tetrahedral coordinate sites.