Stress relaxation of polybutadiene at large deformation. Measurements of stress and birefringence in shear and elongation

Abstract

Abstract The rheological behavior of an uncrosslinked polybutadiene on sudden application of finite strain was examined. The shear stress σ, two components of birefringence, and the extinction angle were measured in shear (magnitude of shear γ ≤ 3.5) and tensile stress and the birefringence were measured in uniaxial elongation (elongation ratio λ ≤ 3.8). Measurements were performed at 30°C with a tensile tester equipped with appropriate sample holders. The stress‐optical coefficient was 3.01 × 10 −9 Pa −1 . The first and second normal‐stress differences v 1 and v 2 were separately evaluated with the use of stress‐optical law. The Lodge—Meissner relation v 1 = γσ held good. The ratio v 2 / v 1 was independent of time and varied from about −0.3 to −0.2 with increasing γ in the range of measurements. Each of the stress components was factored into a function of strain and one of time, and the latter was common to all the stress components. Simple formulas were proposed to represent stress components in step deformations.