Pulsed-laser-deposited epitaxial Sr2FeMoO6−y thin films: Positive and negative magnetoresistance regimes

Abstract

Epitaxial thin films of ordered double-perovskite Sr2FeMoO6−y are deposited on (001) SrTiO3 substrates by pulsed-laser deposition using a two step growth process. Selection of growth conditions is found to lead to either highly conductive metallic thin films (residual resistivity of about 1 μΩ cm) or semiconducting films. The metallic films show a positive magnetoresistance (MR) as high as 35%, while the semiconducting films show a negative MR of −3%, at a temperature of 5 K and a field of 8 T.