High critical current density in epitaxial HgBa2CaCu2OX thin films

Abstract

High quality superconducting HgBa2CaCu2Ox (Hg-1212) thin films have been reproducibly fabricated using cation-exchange method. The thin films have pure Hg-1212 phase and have smooth surface morphology. The superconducting transition temperatures of these films are in the range of 120–124 K. The critical current density Jc is up to 3.2×106 A/cm2 at 77 K and drops only by a factor of 2 at 100 K and self field. At 110 K, a Jc of 7.8×105 A/cm2 has been obtained. X-ray diffraction pole figures show that these films are epitaxially grown on LaAlO3(001) substrates, which is consistent with a χmin of 19% obtained using Rutherford backscattering/channeling analysis.