Infrared quantum cutting in Tb3+,Yb3+ codoped transparent glass ceramics containing CaF2 nanocrystals

Abstract

Tb 3 + – Yb 3 + codoped transparent oxyfluoride glass ceramics containing CaF2 nanocrystals were synthesized. The formation of CaF2 nanocrystals in the glass ceramics was confirmed by x-ray diffraction and high resolution transmission electron microscopy. The incorporation of Tb3+ and Yb3+ into CaF2 nanocrystal lattice was confirmed by energy dispersive spectroscopy. Infrared quantum cutting involving Yb3+ 950–1100nm (F5∕22→F7∕22) emission was achieved upon the excitation of D45 energy level of Tb3+ at 484nm. The photoluminescence properties have been studied for these glass ceramics. Yb3+ concentration dependent quantum efficiency was calculated, and the maximum efficiency approaches 155% before reaching concentration quenching threshold.