nce in thermal properties can be related to the average gray phonon mean free path in graphene, which has been estimated to be around ∼800 nm at room temperature. The thermal contact resistance of composites with graphene fillers of 1200 nm lateral dimensions was also smaller than that of composites with graphene fillers of 400 nm lateral dimensions. The effects of the filler loading fraction and the filler size on the thermal conductivity of the composites were rationalized within the Kanari model. The obtained results are important for the optimization of graphene fillers for applications in thermal interface materials for heat removal from high-power-density electronics.22:T489,We report on the fabrication and characterization of electronic devices printed with inks of quasi-one-dimensional (1D) van der Waals materials. The quasi-1D van der Waals materials are characterized by 1D motifs in their crystal structure, which allow for their exfoliation into bundles of atomic chains. The ink was prepared by the liquid-phase exfoliation of crystals of TiS₃ into quasi-1D nanoribbons dispersed in a mixture of ethanol and ethylene glycol. The temperature-dependent electrical measurements indicate that the electron transport in the printed devices is dominated by the electron hopping mechanisms. The low-frequency electronic noise in the printed devices is of 1/f^γ-type with γ ∼ 1 near-room temperature (f is the frequency). The abrupt changes in the temperature dependence of the noise spectral density and γ parameter can be indicative of the phase transition in individual TiS₃ nanoribbons as well as modifications in the hopping transport regime. The obtained results attest to the potential of quasi-1D van der Waals materials for applications in printed electronics.23:T4e7,We report on the preparation of inks containing fillers derived from quasi-two-dimensional charge-density-wave materials, their application for inkjet printing, and the evaluation of their electronic properties in printed thin-film form. The inks were prepared by liquid-phase exfoliation of CVT-grown 1T-TaS₂ crystals to produce fillers with nm-scale thickness and μm-scale lateral dimensions. Exfoliated 1T-TaS₂ was dispersed in a mixture of isopropyl alcohol and ethylene glycol to allow fine-tuning of filler particles thermophysical properties for inkjet printing. The temperature-dependent electrical and current fluctuation measurements of printed thin films demonstrated that the charge-density-wave properties of 1T-TaS₂ are preserved after processing. The functionality of the printed thin-film devices can be defined by the nearly commensurate to the commensurate charge-density-wave phase transition of individual exfoliated 1T-TaS₂ filler particles rather than by electron-hopping transport between them. The obtained results are important for the development of printed electronics with diverse functionality achieved by the incorporation of quasi-two-dimensional van der Waals quantum materials.24:T402,We report on the preparation of flexible polymer composite films with aligned metallic fillers composed of atomic chain bundles of quasi-one-dimensional (1D) van der Waals material, tantalum triselenide (TaSe₃). The material functionality, embedded at the nanoscale level, is achieved by mimicking the design of an electromagnetic aperture grid antenna. The processed composites employ chemically exfoliated TaSe₃ nanowires as the grid building blocks incorporated within the thin film. Filler alignment is achieved using the "blade coating" method. Measurements conducted in the X-band frequency range demonstrate that the electromagnetic transmission through such films can be varied significantly by changing the relative orientations of the quasi-1D fillers and the polarization of the electromagnetic wave. We argue that such polarization-sensitive polymer films with unique quasi-1D metallic fillers are applicable to advanced electromag

	Year	Citations

About