21:T478,Single-molecule magnet (SMM) properties of crystals of a terbium(III)-phthalocyaninato double-decker complex with different molecular packings (1: TbPc₂, 2: TbPc₂·CH₂Cl₂) were studied to elucidate the relationship between the molecular packing and SMM properties. From single crystal X-ray analyses, the high symmetry of the coordination environment of 2 suggested that the SMM properties were improved. Furthermore, the shorter intermolecular Tb-Tb distance and relative collinear alignment of the magnetic dipole in 2 indicated that the magnetic dipole-dipole interactions were stronger than those in 1. This was confirmed by using direct current magnetic measurements. From alternating current magnetic measurements, the activation energy for spin reversal for 1 and 2 were similar. However, the relaxation time for 2 is three orders of magnitude slower than that for 1 in the low-T region due to effective suppression of the quantum tunneling of the magnetization. These results suggest that the SMM properties of TbPc₂ highly depend on the molecular packing.22:T557,The Li₃MX₆ compounds (M=Sc, Y, In; X=Cl, Br) are known as promising ionic conductors due to their compatibility with typical metal oxide cathode materials. In this study, we have successfully synthesized γ-Li₃ScCl₆ using high pressure for the first time in this family. Structural analysis revealed that the high-pressure polymorph crystallizes in the polar and chiral space group P6₃mc with hexagonal close-packing (hcp) of anions, unlike the ambient-pressure α-Li₃ScCl₆ and its spinel analog with cubic closed packing (ccp) of anions. Investigation of the known Li₃MX₆ family further revealed that the cation/anion radius ratio, r_M/r_X, is the factor that determines which anion sublattice is formed and that in γ-Li₃ScCl₆, the difference in compressibility between Sc and Cl exceeds the ccp r_M/r_X threshold under pressure, enabling the ccp-to-hcp conversion. Electrochemical tests of γ-Li₃ScCl₆ demonstrate improved electrochemical reduction stability. These findings open up new avenues and design principles for lithium solid electrolytes, enabling routes for materials exploration and tuning electrochemical stability without compositional changes or the use of coatings.

	Year	Citations

About