This paper investigates the effect of the ratio of ammonium nitrate (AN) on the structural, microstructural, magnetic, and alternating current (AC) conductivity properties of barium hexaferrite (BaFe₁₂O₁₉). The BaFe₁₂O₁₉ were prepared by using the salt melt method. The samples were synthesized using different powder-to-salt weight ratio variations (1:3, 1:4, 1:5, 1:6 and 1:7) of BaCO₃ + Fe₂O₃ and ammonium nitrate salt. The NH₄NO₃ was melted on a hot plate at 170 °C. A mixture of BaCO₃ and Fe₂O₃ were added into the NH₄NO₃ melt solution and stirred for several hours using a magnetic stirrer under a controlled temperature of 170 °C. The heating temperature was then increased up to 260 °C for 24 hr to produce an ash powder. The x-ray diffraction (XRD) results show the intense peak of BaFe₁₂O₁₉ for all the samples and the presence of a small amount of the impurity Fe₂O₃ in the samples, at a ratio of 1:5 and 1:6. From the Fourier transform infra-red (FTIR) spectra, the band appears at 542.71 cm - 1 and 432.48 cm - 1 , which corresponding to metal⁻oxygen bending and the vibration of the octahedral sites of BaFe₁₂O₁₉. The field emission scanning electron microscope (FESEM) images show that the grains of the samples appear to stick each other and agglomerate at different masses throughout the image with the grain size 5.26, 5.88, 6.14, 6.22, and 6.18 µm for the ratios 1:3, 1:4, 1:5, 1:6, and 1:7 respectively. From the vibrating sample magnetometer (VSM) analysis, the magnetic properties of the sample ratio at 1:3 show the highest value of coercivity H_c of 1317 Oe, a saturation magnetization M_s of 91 emu/g, and a remnant M_r of 44 emu/g, respectively. As the temperature rises, the AC conductivity is increases with an increase in frequency.

	Year	Citations

About