21:T469,A dislocation model, accurately describing the uniaxial plastic stress-strain behavior of dual phase (DP) steels, is proposed and the impact of martensite content and ferrite grain size in four commercially produced DP steels is analyzed. It is assumed that the plastic deformation process is localized to the ferrite. This is taken into account by introducing a nonhomogeneity parameter, f(ε), that specifies the volume fraction of ferrite taking active part in the plastic deformation process. It is found that the larger the martensite content the smaller the initial volume fraction of active ferrite which yields a higher initial deformation hardening rate. This explains the high energy absorbing capacity of DP steels with high volume fractions of martensite. Further, the effect of ferrite grain size strengthening in DP steels is important. The flow stress grain size sensitivity for DP steels is observed to be 7 times larger than that for single phase ferrite.22:T46e,Friction stir welding (FSW), a solid-state joining technique, is being extensively used in similar as well as dissimilar joining of Al, Mg, Cu, Ti, and their alloys. In the present study, friction stir welding of two aluminium alloys—AA6061 and AA5052—was carried out at various combinations of tool rotation speeds and tool traverse speeds. The transverse cross-section of the weld was used for optical as well as electron microscopy observations. The microstructural studies were used to get an indication of the extent of material mixing both at the macro- and microscales. It was observed that, at the interface region, both materials exhibited similar texture despite the nonrigorous mixing of the materials in the nugget. The extent of interdiffusion of alloying elements at the interface was studied using electron probe microanalysis. The tensile testing evaluation of these specimens showed good mechanical properties. The interdiffusion of alloying elements and development of similar orientations in the nugget could have contributed to the better tensile properties of the friction-stir-welded AA5052-AA6061 specimens.23:T447,A study was carried out on aging behaviour of a 6082 alloy processed by two different severe plastic deformation techniques: ECAP and asymmetric rolling. Both techniques were able to generate an ultrafine-grained structure in samples processed at room temperature. It was stated that severe straining promotes marked changes in the postdeformation aging kinetics. The peaks of β ′′/ β ′ transition phases were anticipated and of progressively reduced intensity over the coarse grained alloy. A further peak accounting for onset of recrystallization also appeared in the most severely deformed samples. Full consistency in peak shape and position was found when comparing materials processed by ECAP and asymmetric rolling. Isothermal aging treatments performed at 180°C revealed that in the severely deformed samples, aging became so fast that the hardness curves continuously decreased due to overwhelming effects of structure restoration. On the contrary, aging at 130°C offers good opportunities for fully exploiting the precipitate hardening effects in the ultrafine-grained alloy.24:T4b5,Mill scale is one of waste materials which is produced as a result of hot rolling of steel in all steel companies. On the other hand, mill scale is considered a rich iron source with minimum impurities. This work aims at conversion of mill scale by adjusting smelting processes to produce different valuable products. The smelting processes were carried out using carbothermic reduction in a submerged arc furnace. Two carbonaceous reducing agents and different fluxing materials have been used to adapt optimum smelting process condition. A maximum iron recovery of 83% was obtained by using graphite compared with 76% obtained by using coke. Low sulphur content (≤0.02 wt% S) can be attained by using g

#	Concept	H-Index	Publications	Citations
1	Engineering	18	33	1.3K
2	Chemical Engineering	8	8	156
3	Applied Physics	6	6	109
4	Natural Sciences	1	1	15
5	Biomedical Engineering	1	1	553

	Year	Citations

About

Top Concepts