Experimental investigation of fracture in an advanced fiber composite.

Abstract

Pilot tests were run to determine the applicability of the concepts of linear elastic fracture mechanics (LEFM) to the description of the mechanical behavior of initially cracked specimens of advanced fiber composite laminates. It was found that the failure mechanisms in such specimens were largely crack-dominated and that LEFM procedures were applicable even when the apparent failure mechanism was not explicitly dominated by a starter crack.