1e:T48c,The lithium-sulfur battery holds a high theoretical energy density, 4-5 times that of today's lithium-ion batteries, yet its applications have been hindered by poor electronic conductivity of the sulfur cathode and, most importantly, the rapid fading of its capacity due to the formation of soluble polysulfide intermediates (Li(2)S(n), n = 4-8). Despite numerous efforts concerning this issue, combatting sulfur loss remains one of the greatest challenges. Here we show that this problem can be effectively diminished by controlling the sulfur as smaller allotropes. Metastable small sulfur molecules of S(2-4) were synthesized in the confined space of a conductive microporous carbon matrix. The confined S(2-4) as a new cathode material can totally avoid the unfavorable transition between the commonly used large S(8) and S(4)(2-). Li-S batteries based on this concept exhibit unprecedented electrochemical behavior with high specific capacity, good cycling stability, and superior rate capability, which promise a practicable battery with high energy density for applications in portable electronics, electric vehicles, and large-scale energy storage systems.1f:T46f,Because of their high theoretical energy density and low cost, lithium-sulfur (Li-S) batteries are promising next-generation energy storage devices. The electrochemical performance of Li-S batteries largely depends on the efficient reversible conversion of Li polysulfides to Li₂S in discharge and to elemental S during charging. Here, we report on our discovery that monodisperse cobalt atoms embedded in nitrogen-doped graphene (Co-N/G) can trigger the surface-mediated reaction of Li polysulfides. Using a combination of operando X-ray absorption spectroscopy and first-principles calculation, we reveal that the Co-N-C coordination center serves as a bifunctional electrocatalyst to facilitate both the formation and the decomposition of Li₂S in discharge and charge processes, respectively. The S@Co-N/G composite, with a high S mass ratio of 90 wt %, can deliver a gravimetric capacity of 1210 mAh g^-1, and it exhibits an areal capacity of 5.1 mAh cm^-2 with capacity fading rate of 0.029% per cycle over 100 cycles at 0.2 C at S loading of 6.0 mg cm^-2 on the electrode disk.20:T59b,

	Year	Citations

References