1d:T502,Abstract The low power conversion efficiency (PCE) of tin‐based hybrid perovskite solar cells (HPSCs) is mainly attributed to the high background carrier density due to a high density of intrinsic defects such as Sn vacancies and oxidized species (Sn 4+ ) that characterize Sn‐based HPSCs. Herein, this study reports on the successful reduction of the background carrier density by more than one order of magnitude by depositing near‐single‐crystalline formamidinium tin iodide (FASnI 3 ) films with the orthorhombic a ‐axis in the out‐of‐plane direction. Using these highly crystalline films, obtained by mixing a very small amount (0.08 m ) of layered (2D) Sn perovskite with 0.92 m (3D) FASnI 3 , for the first time a PCE as high as 9.0% in a planar p–i–n device structure is achieved. These devices display negligible hysteresis and light soaking, as they benefit from very low trap‐assisted recombination, low shunt losses, and more efficient charge collection. This represents a 50% improvement in PCE compared to the best reference cell based on a pure FASnI 3 film using SnF 2 as a reducing agent. Moreover, the 2D/3D‐based HPSCs show considerable improved stability due to the enhanced robustness of the perovskite film compared to the reference cell.1e:T47f,Piezoelectric and ferroelectric properties in the two-dimensional (2D) limit are highly desired for nanoelectronic, electromechanical, and optoelectronic applications. Here we report the first experimental evidence of out-of-plane piezoelectricity and ferroelectricity in van der Waals layered α-In₂Se₃ nanoflakes. The noncentrosymmetric R3m symmetry of the α-In₂Se₃ samples is confirmed by scanning transmission electron microscopy, second-harmonic generation, and Raman spectroscopy measurements. Domains with opposite polarizations are visualized by piezo-response force microscopy. Single-point poling experiments suggest that the polarization is potentially switchable for α-In₂Se₃ nanoflakes with thicknesses down to ∼10 nm. The piezotronic effect is demonstrated in two-terminal devices, where the Schottky barrier can be modulated by the strain-induced piezopotential. Our work on polar α-In₂Se₃, one of the model 2D piezoelectrics and ferroelectrics with simple crystal structures, shows its great potential in electronic and photonic applications.

	Year	Citations

References